Warm Forming Aluminum Sheet

Formability was studied by forming rectangular parts at a rapid rate of 1 s 1 using internally heated punch and die for both isothermal and non.

Warm forming aluminum sheet.

Investigated aluminum sheet metal materials. Developed fully automated warm forming cell capable of demonstrating the process under run at rate conditions at 5 jobs per minute for both aluminum and magnesium. The first approach is a warm forming route to form sheets in t6 temper state with high tensile strength at temperatures between 150 c and 300 c. This video shows a warm forming trial at ewi forming center with aa 6xxx 7xxx.

Aluminum at elevated temperatures. Because of the complexity of various parts and lack of knowledge base further development work is needed to establish design guidelines for warm forming. Warm forming of aluminum alloys offers the possibility of drawing complex aluminum sheet products which cannot be manufactured at room temperature without extra forming and joining operations. Ing warm forming does not impart high ductility stretch formabili ty to the material.

Warm forming technology is a promising approach to improve the formability of peak aged 7075 aluminum alloys aa7075 t6 5 6 7 8 where the aa7075 t6 blank is heated to target temperatures. However for a general purpose aluminum alloy warm forming offers better deep drawability than cold forming 3 9 warm forming has not yet been applied in automotive parts pro duction. In fact elevating the temperature or warm forming of aluminum sheet at reasonable production rates and acceptable costs has become a realistic alternative to straight stamping. Developed finite element prediction of forming and failure during warm forming.

Aluminum sheet alloys only typically posses moderate formability at room temperature limiting their design applications. Established forming process limits for both commercial al and mg sheet. Al 5754 al 5182 containing 1 mn and al 6111 t4. Warm forming of aluminum sheet has emerged as a way to increase ductility and formability.

Introduction sheet metal aluminum alloys are prime candidates for use in the automotive industry because of their good strength and stiffness to weight ratios. Warm forming of these alloys can significantly improve their formability and this is the main. Li and ghosh 2004 also investigated biaxial warm forming behavior in the temperature range 200 350 c for three automotive aluminum sheet alloys.